| Customization: | Available |
|---|---|
| Material: | Stainless Steel |
| Refractoriness (℃): | 1580< Refractoriness< 1770 |
|
Still deciding? Get samples of US$ 0/KG
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Melt Extracted Stainless Steel Fiber
Chemical composition
| Steel Grade | C | Si | S | P | Mn | Ni | Cr | Mo | V | Cu | Ti | Co | B |
| 446 | <0.30 | <3.0 | <0.03 | <0.04 | 1.0~1.5 | 0.45 | 24-27 | - | - | <0.25 | - | - |
<0.003 |
The Specification Of Melt-extraction SSF
| Specification | Cross-section areas(mm2) | Equivalent diameter(mm) | Cross-section size(mm) | Length(mm) | Configuration & shape |
| 0.5*20 | 0.2 | 0.5 | 0.2*1 | 20 | Straight |
| 0.5*25 | 25 | ||||
| 0.5*35 | 35 |
Technical Properties And Performance
| Alloy | 446 | |
| Melt temperature range | ºC | 1430~1510 |
| Thermal conductivity @ 540ºC | Kcal/m2 · h · ºC | 69.8 |
| Modulus of elasticity @ 870ºC | × 106kg/cm ² | 0.984 |
| Fiber tensile strength @ 870ºC | kg/cm ² | 540 |
| Coef. of thermal expansion @870ºC | × 10-6/ºC | 13.14 |
| Critical oxidation temperature | ºC | 1200 |
|
Increased flexural strength of 60% alumina Refractory fired at 870ºC(1600ºF)for 8hrs 1.3.V% fiber |
1.15 | |
| Increased energy absorption 60% alumina ref. fired at 870ºC(1600ºF) for 8 hrs | 10-12 | |
| Carburization increase in carbon content% in 25 hrs @982ºC(1800ºF) | 0.07 | |
| Corrosion rate in Coke oven gas at 982ºC(1800ºF) | Mils/yr | 14 |
| Corrosion rate nitriding | Mils/yr | 1120 |
| Oxidation cycling coditions 1000 hrs wt % loss @ 982ºC(1800ºF) | 4% | |
The properties and performance of refractory materials applying to various beating furnaces kilns and coke ovens should be greatly improved if SSF will be mixed with.
Today SSF reinforcement is finding its way into every parts of modern industries. They can be concluded as follow:
1)Metallurgical industry
blast-heating cupola, iron smelting furnaces, open hearth furnaces, convertors electrical furnaces, spray gun for refining of metal out of furnace, sintering furnaces and kilns. heaters for steel rolling, including lining, furnace-door and wrapping covers around water cycling pipes.
2)Oil oven, and kilns.
3)Furnaces and kilns in ceramic,glass and enamel industries.
4)Rotary and standing kilns in cement industry.
5)Forging heaters and boilers for power plant.
6)Furnaces and kilns in other industries.